Position：Home > PRODUCT > Flame Retardant Masterbatch

F68-112

1.  This is a compound flame retardant system，BDDP based by adding effective synergist and stabilizer. Dosage 8% will make the sample (3.0MM)achieve level UL94V0 ,compare with simple using BDDP it improved the flame retardant efficiency and reduced dosage of Sb2O3.

 

2.  Product Character:

Appearance：White loose powder

Br content：60%

Weight loss:≤0.3%

Melting point：110℃ Begin to softening and melting

Decomposition temperature：285℃，mass loss 5%：330℃

Dissolubility：Water insoluble,Partly soluble in Dichloroethane、Toluene、Acetone Esters etc。  
    Toxicity LD50（Oral delivery in white mice）＞5000mg/kg（non-toxic）   
    Potential carcinogen ：Non   
    Skin irritation：Non
 

Comparison by using F68-

Index table of comparisons
 
  Performance Powder of HOPP Powder of HOPP
（8%BDDP+Sb2O3）		 Powder of HOPP（6%F68-112+Sb2O3） Powder of HOPP
（8%F68-112+Sb2O3）
1 Melt Index
(g/10min)		 5.8 6.9 6.5 6.8
2 Tensile（Mpa） 31 30 31 30
3 Tensile nominal strain
（%)		  
79		  
70		  
73		  
71
4 Flexural modulus
（GPa）		 1.1 1 1 1
5 Izod impact strength
（KJ/m*m）
A Type Gap
No gap		  


4.1
78.8		  


3.9
85.2		  


3.8
89		  


3.6
83
6 UL-94 Fire resistance
1.6mm
3.0mm		  
 
——
——

v-0
v-2

v-2
v-2

v-2
v-0